Self-leveling cement mix for filling up and sealing diggings of channels, trenches, sewages and the like and for building works in general

ABSTRACT

A self-leveling cement mix employed for filling up and sealing excavations of channels, trenches, sewages and the like and for building works of various kinds. The cement mix includes large-sized sand of various kind having a median grain size of 3 mm, fine-sized sand of various kind having a median grain size of 1.5 mm, volatile ash as a remnant product of coal combustion, conventional type cement, cement aerating agent, fluidifying agent, and water.

FIELD OF THE INVENTION

[0001] The invention relates to a self-leveling cement mix which is employed for filling up and sealing excavations of channels, trenches, sewages and the like and for building works of various kinds.

BACKGROUND OF THE INVENTION

[0002] At the present, for filling up the excavations effected on the ground for laying pipings, sewages and the like, after these pipings, sewages, etc. have been laid they are covered with compacting material so as to keep them in position and to close the excavations, and as material therefor concrete of conventional kind is normally used, which is poured in position, or some embankment earth or loose tombstone material (sand, crushed stone, coarse gravel) is utilized, or a combination of materials, concrete and embankment earth or tombstone material which are suitably mixed with each other are utilized.

[0003] The use of the above-mentioned filling and compacting materials, however, gives raise to some drawbacks. In fact, first of all these materials are not able to perform effective sealing of the pipings, sewages and the like which have been laid underground, due to the difficulty of these materials to distribute themselves for filling all the areas around the pipings and sewages, and under these circumstances inadequate sealing may sometime occur at the junctions of such pipings and sewages, with consequent outgoing and loss of the fluid transported through such pipings and sewages. This phenomenon tends to occur when using both fluid concretes and embankment earth or loose tombstone material, and with these later materials which are denser and less fluid the above phenomenon is particularly emphasized, owing to the greater difficulty of these materials to uniformly distribute themselves on all the positions of pipings and sewages.

[0004] Another drawback of the use of the current materials is due to the difficulty of arranging the excavation filling and sealing material which is submitted to continuous loads produced by vehicular traffic passing over the same material and tends to yield slowly and progressively, particularly in the case in which the material is embankment earth or tombstone material, and this material has been covered with a road surface. Also in this case, the use of compacted tombstone material involves a more accentuated phenomenon, since a slow and progressive crushing in position of the weaker tombstone elements and a penetration of the stiffer tombstone elements on the more yieldable original ground may occur.

[0005] Finally, the use of these filling and sealing materials involves the drawback that the same materials are difficult to remove, when such removal is needed for maintenance or repair works of pipings, sewages etc. and it is very difficult and burdensome if the used material is concrete.

SUMMARY OF THE INVENTION

[0006] The object of the present invention is to eliminate the above drawbacks and applicative limits deriving from the use of the current materials, by means of the use of the cement composition according to the present invention, which is adapted to provide for an effective filling, compacting and sealing of excavations for piping, sewages etc., laid underground, and it is absolutely stable over time and easily removable in the cases of need for performing the above-described works.

DETAILED DESCRIPTION OF THE INVENTION

[0007] The invention will be better understood from the following description, given solely by way of not-limitative example. The self-leveling cement mix in accordance to the invention is constituted substantially by the following components:

[0008] 1) large-sized sand of various kind, with median grain size preferably of 3 mm;

[0009] 2) fine-sized sand of various kind, with median grain size preferably of 1.5 mm;

[0010] 3) volatile ash, this term being intended as a remnant product of coal combustion, as for example in thermoelectric power plants;

[0011] 4) cement of conventional type and preferably but not necessarily Portland 325 cement;

[0012] 5) aerating agent for cements;

[0013] 6) fluidifying agent, constituted by a mixture of surface-active agents and dispersants; and

[0014] 7) water.

[0015] The above components are mixed with each other at ambient pressure and temperature, with the following proportions:

[0016] 1) large-sized sand from 1 to 10,000 Kg/cu.m., preferably 840 Kg/cu.m.;

[0017] 2) fine-sized sand from 1 to 10,000 Kg./cu.m., preferably 780 Kg/cu.m.;

[0018] 3) volatile ash from 0,5 to 90 Kg/cu.m., preferably 25 Kg/cu.m.;

[0019] 4) cement from 0.5 to 500 Kg/cu.m., preferably 60 Kg/cu.m.;

[0020] 5) aerating agent for cements from 0,1 liter/cu.m. to 50 liter/cu.m., preferably 0,8 liter cu.m.;

[0021] 6) fluidifying agent from 0,1 liter/cu.m. to 50 liter cu.m., preferably 1,8 liter cu.m,;

[0022] 7) water from 1 Kg/cu.m. to 500 Kg/cu.m. preferably 155 Kg/cu.m.

[0023] Instead of sands, as components under 1) and 2) also inert materials of various kind for the building industry, with the same proportion may be used. Instead of volatile ash, as component under 3)also hydraulic lime, with the same proportion, may be used. As aerating agent for cement, also the product named RH878, of the firm MAC S.p.A., via Vic. Corti 21, Treviso, Italy, may be advantageously used and as fluidifying agent the product named MVR of the above same firm may be advantageously used. As alternative, as aerating agent and fluidifying agent also the product named RIVEREN ITI, 27P of the firm Rental Colloid of Valdobbiadene (TV), via Pra Fontana 55/1, Italy may be advantageously used.

[0024] The resulting cement composition is used for filling up and compacting the excavations where pipings, sewages and the like have been laid underground, and thanks to its excellent fluidity it has the capacity to distribute itself to all positions, thereby filling up and sealing effectively all the pipings and sewages laid underground, as well as the effected excavations, thereby preventing any outgoing and loss of the fluids transported through the pipings and sewages, as well as permitting a quick settling of the material without possibility that it may yield subsequently, after hardening thereof, so as to ensure a high ground compactness and an absolute stability over time.

[0025] Finally, thanks to the limited resistance to tensile stress of this material, it may be easily removed in a simple and quick manner without difficulty, when necessary to perform subsequent maintenance or repair works of the pipings and sewages.

[0026] The cement mix according to the invention may be advantageously utilized also for further applications, such as for example:

[0027] a) for floor foundations, whereby it allows a perfect leveling of the laying plane surfaces of the foundations for buildings, swimming pools, sheds, etc., by replacing the conventional leans;

[0028] b) for bases, whereby it is particularly suitable in the building industry for manufacturing of floor bases;

[0029] c) insulating mix, whereby it is employed alone or mixed with other light components (expanded clay, vermiculite, pumice, lapilli) for manufacturing of high insulating elements, for elevated structures (filling of box-like masonries) and horizontal or non-horizontal structures (flat roofs or roofs with variable inclination);

[0030] d) filling up of hollow spaces in the ground, e.g. of old reservoirs to make inert, etc.,

[0031] e) sound absorbing panels for sheds and building industry in general;

[0032] f) civil and road building, bridges, viaducts, etc.

[0033] Accordingly, while a few embodiments of the present invention have been shown and described, it is to be understood that many changes and modifications may be made thereunto without departing from the spirit and scope of the invention as defined in the appended claims. 

What is claimed is:
 1. Self-leveling cement mix for filling up and sealing excavations of channels, trenches, sewages and the like, after the pipings, sewages and the like have been laid, and for building works in general characterized by mixing the following components: a) large-sized sand or inert materials of various kinds for building industry, with a median grain size preferably of 3 mm; b) fine-sized sand or inert materials of various kinds for building industry, with a median grain size of 1.5 mm; c) ash derived from coal combustion; d) cement of conventional type and preferably 325 Portland cement; e) aerating agent for cements; f) fluidifying agent; and g) water, wherein this mixing occurs preferably at ambient pressure and temperature.
 2. Cement mix according to claim 1, characterized in that said components are mixed with each other with the following proportions: a) from 1 to 10,000 Kg/cu.m., preferably 840 Kg/cu.m., b) from 1 to 10,0000 Kg/cu.m., preferably 780 Kg/cu.m., c) from 0.5 to 90/Kg/cu.m., preferably 25 Kg/cu.m., d) from 0.5 to 500 Kg/cu.m., preferably 60 Kg/cu.m., e) from 0.1 liter/cu.m. to 50 liter/cu.m., preferably 0.8 liter/cu.m., f) from 0.1 liter/cu.m. to 50 liter/cu.m., preferably 1.8 liter/cu.m., g) from 1 Kg/cu.m. to 500 Kg/cu.m., preferably 155 Kg/cu.m.
 3. Cement mix according to claim 2, characterized in that as component under c) also hydraulic lime with the same proportions may be used.
 4. Cement mix according to claim 2, characterized in that as component under e) also the product named RH878 of the firm Mac S.p.A., via Vic. Corti 21, Treviso, Italy may be used.
 5. Cement mix according to claim 2 characterized in that as component under f) also the product named MVR of the firm MAC S.p.A., via Vic. Corti 21, Treviso, Italy may be used.
 6. Cement mix according to claim 2, characterized in that as component under e) and f) also the product named RIVEREN ITL 27P of the firm Rental Collid, via Pra Fontana 55/1, Valdobbiadene (TV), Italy may be used of which the component under f) is constituted by a mixture of surface-active agents and dispersants. 